Key features
- Excellent adhesion against PE, EVOH, and PA
- Very good optical properties
- Good performance in machine direction oriented film and bioriented blown film
Yparex 8903 E is a maleic anhydride functionalized VLDPE, produced by reactive extrusion. It has been primarily designed to act as an adhesive in multilayer oriented films to ensure adhesion between PE, EVOH and PA.
| Thermal Properties | Typical Value | Unit SI | Test Method |
|---|---|---|---|
| Melting Temperature (10°C/min) | 124 | °C | ISO 11357-1/-3 |
| Vicat Softening Temperature 50°C/h 10N | 55 | °C | ISO 306 |
| Physical Properties | Typical Value | Unit SI | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) 190°C/2.16kg | 3.2 | g/10 min | ISO 1133 |
| Enthalpy of Melting | 72 | kJ/kg | ISO 11357-1/-3 |
| Density | 0.890 | g/cm³ | ISO 1183 |
Comprehensive material safety data sheets are provided to recommend safe practices during usage. For easy handling and storage, this grade is supplied as f ree-flowing pellets normally packed in 20 kg bags (65 bags per pallet) or 500 kg boxes.
Compounding parameters that can lead to optimized performance include extruder type, screw design, barrel temperature, screw speed, throughput, residence time and material feeding sequence. Our experienced technical service engineers and chemists are always on hand to help you in achieving the best performance from your processing and compounding operations.
Africa & Middle East, Europe, North America, Asia Pacific, Latin America.
Product may not be available in one or more countries in the identified availability regions. Please contact your sales representative for complete country availability.
This product, including the product name, shall not be used or tested in any medical application without the prior written acknowledgement of The Compound Company as to the intended use. For detailed Product Stewardship information, please contact Customer Service.
Yparex 89103 E (formerly 0H207) is LLDPE based grade for oriented film.