Key features
- Excellent adhesion against fabrics, polyolefins, EVOH, PA and aluminium
- Good processability in extrusion coating
- High processing temperatures possible
- Low neck-in and good web stability
Yparex 9508 is a maleic anhydride functionalized EBA (ethylene butyl acrylate), produced by reactive extrusion. It has been primarily designed to act as an adhesive in multilayer film to ensure adhesion between PE, EVOH, PA and aluminium.
| Thermal Properties | Typical Value | Unit SI | Test Method |
|---|---|---|---|
| Melting Temperature (10°C/min) | 92 | °C | ISO 11357-1/-3 |
| Vicat Softening Temperature 50°C/h 10N | 65 | °C | ISO 306 |
| Physical Properties | Typical Value | Unit SI | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) 190°C/2.16kg | 8.0 | g/10 min | ISO 1133 |
| Enthalpy of Melting | 63 | kJ/kg | ISO 11357-1/-3 |
| Density | 0.928 | g/cm³ | ISO 1183 |
Comprehensive material safety data sheets are provided to recommend safe practices during usage. For easy handling and storage, this grade is supplied as f ree-flowing pellets normally packed in 20 kg bags (65 bags per pallet) or 500 kg boxes.
Compounding parameters that can lead to optimized performance include extruder type, screw design, barrel temperature, screw speed, throughput, residence time and material feeding sequence. Our experienced technical service engineers and chemists are always on hand to help you in achieving the best performance from your processing and compounding operations.
Africa & Middle East, Europe, North America, Asia Pacific, Latin America.
Product may not be available in one or more countries in the identified availability regions. Please contact your sales representative for complete country availability.
This product, including the product name, shall not be used or tested in any medical application without the prior written acknowledgement of The Compound Company as to the intended use. For detailed Product Stewardship information, please contact Customer Service.
Yparex 9503 S is a ready-to-use PE-based tie resin for extrusion coating, transparent, flexible, adhesion to PE (polyethylene), PA (polyamide) and aluminium.
Yparex 9207 is a maleic anhydride functionalized LDPE, produced by reactive extrusion.
Yparex RENEW 0H218 is a ready-to-use PE bio-based tie resin for extrusion coating.